VISTALON by EXXONMOBIL
Vistamaxx™*: | Application | |
| Vistamaxx™ propylene-based elastomers are produced by ExxonMobil Chemical using proprietary metallocene catalyst technology | – Elasticity | – Stretch film |
| – Softness | – Elastic hygiene film | |
| – Sealability | – Surface protection film | |
| – Adhesion | – Stretch hood film | |
| Composition and structure: | – Toughness | – Heat sealable cast PP (cPP) film |
| • Semicrystalline copolymers of propylene and ethylene | – Cling / tackiness | – Heat sealable |
| • High propylene levels (>80 wt%) with isotactic stereochemistry | – BOPP film | |
| • Uniform inter- and intramolecular composition and crystallinity distribution | – Heat shrinkable display films (double bubble) | |
| • Crystallinity is modulated with ethylene: | – Extrusion lamination in flexible packaging | |
| • 5-25% crystallinity, large amorphous fraction | – Polypropylene raffia tapes | |
| • Very soft | – Extrusion coated and laminated PP woven sacks | |
| • Elasticity unlike other polyolefin polymers, blends or alloys | – Industrial fabrics extrusion coating | |
| – HDPE shopper and garbage bags |
| Grade name | Polymer Types | Density (g/cm3) | M.I.(1) ,(g/10 min), 230 ?C | MFR, (g/10 min), 220 °C | T.S.(3) (kg/cm2), ASTM D638 | T.S.(3) , (MPa) Break, ISO 527 or ASTM D638 | T.M.(5) (MPa),ISO 527 | F.M.(6) (MPa) / (kg/cm2), ASTM D790 | Elongation(13) % | Hardness (Shore) (15) Shore A | Hardness (Shore) (15) Shore D | E.C.(19) (%) | Color | Dosage Recommend (%) | Physical Form (Beads, Pellets, Powder, Flakes) | Product Description |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
VISTAMAXX 3000 | PP METALLOCENE | 0.873 | 3.6 | 8 | 5.22 (ASTM D638) | 59.3 | 0.48 | 11 | Natural | 5-50% | Pellets | PP-Base Elastomer is an olefin elastomer. | ||||
VISTAMAXX 3020 FL | PP METALLOCENE | 0.874 | 1.1 | 4.65 | 59.7 | 1756 | 34 | Natural | PP-Base Elastomer, Excellent Elastomeric properties, Flexibility, Transparency and Impact Performance. Suitable for Polyolefinic Blends where a balance of Flexibility, Transpaency and Impact Performance is required.Tie layer for extrusion lamination and extrusion coating of PP woven sack, increase adhesion strength,improve tenacity, load more filler and recycle.For shopping bag can load more filler. Packaging for low SIT and easy peel application | |||||||
VISTAMAXX 3980 FL | PP METALLOCENE | 0.878 | 3.7 | 5.65 | 110 | 1682 | 40 | Natural | ||||||||
VISTAMAXX 6102 | PP METALLOCENE | 0.862 | 1.4 | 3 | 19.8 | 12.3 | >2,000 | 16 | Natural | 5-50% | Pellets | PP-Base Elastomer is an olefin elastomer. | ||||
VISTAMAXX 6102 (650 KG/OCTABIN BOX) | PP METALLOCENE | 0.862 | 1.4 | 3 | 19.8 | 12.3 | >2,000 | 16 | Natural | 5-50% | Pellets | PP-Base Elastomer is an olefin elastomer. | ||||
VISTAMAXX 6102 FAR | PP METALLOCENE | 0.862 | 3 | 2.24 | 12.3 | 2000 | 66 | Natural | ||||||||
VISTAMAXX 6202 | PP METALLOCENE | 0.861 | 7.4 | 18 | 17.3 | 11 | Natural | 5-50% | Pellets | PP-Base Elastomer is an olefin elastomer. | ||||||
VISTAMAXX 6202 FAR | PP METALLOCENE | 0.863 | 9.1 | 2.1 | 12.3 | 2000 | 66 | Natural |